Self Leveling Polishable Cement Overlay Wear Topping Material Systems
Polished concrete self-level systems with aggregate for the look of natural polished concrete and a salt and pepper finish. Concrete epoxy primer for use with the polished concrete wear topping self-level overlayment product.
Schonox DSP Plus Polished Overlayment System with Aggregate
Wear Rated, Cement-Based Self-Leveling Concrete Topping with larger aggregate. DSP PLUS provides an extremely dense and durable surface to be polished in interior and exterior areas. DSP PLUS can be installed at a minimum of 3/8″ up to 2″. Designed for a variety of applications over suitable concrete from retail environments, restaurants, public buildings, entryways and offices to warehouse or manufacturing areas with moderate industrial loads. Suitable as a decorative topcoat.
Schonox EPA Rapid Epoxy Moisture Mitigation System
Rapid Curing, Two-Part, Epoxy Based Moisture Mitigation System suitable on porous, unheated concrete slabs to reduce moisture vapor emission rates from 100% RH or 25 lbs./1000 sq.ft./24 hrs to suitable levels before applying Schönox underlayments. Only one coat required to penetrate and to fully seal the substrate. Residual moisture issues in your concrete subfloor as high as 100% RH can be handled with just one coat. No VOC. Low viscosity. High penetration. Choose Schönox EPA Rapid for even tighter project time constraints.
Aqualon L-100 Lithium Silicate Concrete Densifier
Aqualon L-100 is an environmentally friendly, VOC free, lithium silicate concrete floor densifier, hardener, and sealer. Aqualon L-100 is designed to penetrate untreated, bare concrete surfaces providing a permanent gloss, dustproof floor. Polished concrete lithium densifier. Aqualon L-100 reacts quickly with the concrete floor surface to produce an initial and ultimate hardness. Aqualon L-100 lithium silicate concrete densifier shows the great effect when used in conjunction with floor polishing machines, yielding a highly protected, hardened, and densified polished concrete floor.
Non-Film Forming Deep Penetrating Nano Surface Protectant DK-900
DK 900 invisibly protects chemically hardened industrial floors, commercial facilities, machine shops, auto repair facilities, and polished concrete floors from prolonged exposure to oil, salts, and water damage. DK 900 is a dual component, water reducible, multifunctional, concrete protectant that repels oil, salt, de-icing agents, and water. With its roots in Urethane and Acrylic nanotechnology, DK 900 is designed to be minimal/non-film forming on concrete, polished concrete, and natural stone surfaces. Nanotechnology allows for deep penetration into porous substrates DK 900 is excellent as a maintenance guard on existing slabs.
Additional information on these polishable self-level wear topping material systems.
Schonox DSP Plus Polished Overlay Material System with Aggregate
- 7250 psi / 43 N/mm² / 580 kg/cm2 after 28 days
- 4250 psi / 25 N/mm² / 300 kg/cm2 after 1 day
Coverage: Approx. 12 sq.ft. at 3/8“
- EQc2 – 3 points
- Low-Emitting Materials: MRc1 – up to 2 points
- Life-Cycle Impact Reduction: MRc2 – 1 point
- Environmental Product Declaration: MRc4 – 1 point
- Material Ingredients
Pot Life: Approx. 30 minutes
Ready for Grinding: Approx. 24 hours
Shelf Life: 1 year unopened
Working Temperature: 41°F – 90°F
EMICODE EC 1PLUS R: very low emission
For interior and exterior use
Suitable on underfloor heating systems
Suitable for castor wheel loadings at 1/4″
Suitable for use as a commercial wear topping in industrial applications polishing minimum 3/8″
RECOMMENDED APPLICATION DETAILS
Schönox DSP is suitable for filling, smoothing and leveling of substrates under Suitable sealers, densifiers, and coatings when installed as a wear layer or polished topping
PACKAGING: 25 kg / 55 lb. net weight in paper bags
STORAGE: Store in cool and dry conditions.
Shelf life: 12 months unopened
DISPOSAL: Empty packaging and dispose of in accordance with federal, state and local waste disposal regulations.
VOC CONTENT: 0g/l (calculated), SCAQMD 1113
Pot life: approx. 30 minutes at 68°F
Ready for foot traffic: after approx. 2-3 hours
Ready for covering: – after 24 hours up to 1/4″ thickness – after 48 hours up to 1/4″ thickness prior to applying suitable sealers, densifiers and coatings or prior to polishing – for ceramic tiles: when walkable
Working temperature: not below 41°F floor temperature
Coverage: approx. 25-30 sq.ft. per unit at a thickness of 1/4″ (depending on substrate conditions and aggregate used)
Compressive strength (ASTM C109/ mod – air cure only): approx. 40 N/mm² / 7250 psi at 28 days
Flexural strength (ASTM C348): approx. 10 N/mm² / 1500 psi at 28 days
Tensile strength (ASTM C1583): approx. 3 N/mm² / 450 psi after 3 days
Initial Set (ASTM C191): approx. 80 minutes at 70°F
Final set (ASTM C191): approx. 95 minutes at 70°F
UL classified in accordance with ASTM E84 (ANSI/UL 723): Flame Spread 0; Smoke Development 0
Abrasion resistance (ASTM D4060): approx. 1.4 at 28 days
All values are approximate and are subject to local climatic fluctuations based upon conditions at 70°F with an atmosphere of less than 65% relative humidity following the recommended mixing ratio. Do not install underlayment or topping before the substrate has dried thoroughly.
LEED V4 May help contribute to LEED v4 certification of projects in these categories:
EQc2 – 3 points Low-Emitting Materials
MRc1 – up to 2 points Life-Cycle Impact Reduction
MRc2 – 1 point Environmental Product Declaration
MRc4 – 1 point Material Ingredient
Schonox EPA Rapid 100% Solids Epoxy Moisture Mitigation System
Coverage Rate: Approx. 300 sq.ft. per unit; the finished application must cover the substrate completely without any voids or pinholes to ensure moisture vapor suppression!
EQc2 Low-Emitting Materials – 1 to 3 points
Shelf Life: 24 months unopened
Working Time: Approx. 10min. at 65°F
Color: Transparent Amber
Packaging: 2-Component system 7.14 kg / 1.68 gallons component A (resin) in metal canister, 2.86 kg / 0.77 gallons component B (hardener) in metal canister
- solvent-free, 100% solids epoxy
- complies to SCAQMD 1113
- low viscosity
- high penetrating
- problem solver on damp concrete (after the concrete is visually dry and porous)
- resistant to chemical loadings
- for interior and exterior use
To suppress moisture on unheated, moisture resistant, porous concrete with residual moisture up to 100% RH or 25 lbs./1000 sq.ft./24 hrs. before applying SCHÖNOX underlayments prior to installing flexible coverings as well as wood floor
Density: 1.1 kg/l (mixed material)
Storage temperature: not below 41°F
Working time: approx. 10 min. at 65°F
Working temperature: not below 50 °F
floor temperature (recommended: > 65°F, relative humidity <=75%)
Maximum Coverage Rate: approx. 300 sq.ft. per unit; the finished application must cover the substrate
completely without any voids or pinholes to ensure moisture vapor suppression!
Ready for leveling (after back roll): after approx. 2 – 3 hours at 65°F floor temperature
Permeance (ASTM E96): ≤ 0.1 perm
Non Film Forming Deep Penetrating Nano Surface Protectant DK-900
DK 900 is suitable for numerous interior or exterior surfaces including but not limited to polished concrete, broom finish concrete, stained concrete, decorative concrete, exposed concrete, honed and polished travertine, white Carrera marble, natural stone, pavers, synthetic stone, unglazed tile, and brick. It excels in performance on vertical and horizontal surfaces.
DK 900 is a dual component, water reducible, multifunctional, concrete protectant that repels oil, salt, de-icing agents, and water. With its roots in Urethane and Acrylic nanotechnology, DK 900 is designed to be minimal/non-film forming on concrete and natural stone surfaces. Nanotechnology allows for deep penetration into porous substrates DK 900 is excellent as a maintenance guard on existing slabs. DK 900 is suitable for numerous interior or exterior surfaces including but not limited to polished concrete, broom finish concrete, stained concrete, decorative concrete, exposed concrete, honed and polished travertine, white Carrera marble, natural stone, pavers, synthetic stone, unglazed tile, and brick. It excels in performance on vertical and horizontal surfaces.
Water Repellency 24 hours
Recoat window Between 1 – 72 hours
Open time 2 hours with agitation at 20 min. intervals
Avoid Foot Traffic 2 hours or dry to the touch
Chemical and Stain Resistance 168 hours @ 70°F