Products for Stained and Polished Concrete Floors

Need custom colored joint filler or surface repair materials for your colored concrete floor project? You can rely on Metzger/McGuire’s Industry Standard Floor Joint Fillers and Concrete Repair Products to provide your customer with surface restoration products manufactured to exacting color match standards and formulated to last for the life of the floor.

Spal-Pro RS 88 Concrete Floor Joint Filler for High Traffic Polished Concrete Floors

Spal-Pro RS 88 is a 100% solids, two-component heavy duty, semi-rigid polyurea joint filler intended for use in filling and protecting contraction and construction joints in industrial, retail, or commercial polished concrete floors. Shore A Hardness: A86-90. Spal-Pro RS 88 was developed to fill and protect joints in trafficked industrial and retail polished concrete floors. Its primary function is to support such traffic and protect joint edges. Spal-Pro RS 88 is intended for use where final temperatures are from 32˚F to +120˚F. Spal-Pro RS 88 is also ideal for filling random cracks in polished concrete floors.

Information Links:

Edge Pro 80 Concrete Floor Joint Filler For Polished Concrete Floors

Edge-Pro 80 Polyurea Shaves Flush and Protects Joint Edges. Edge-Pro 80 is a two-part, 100% solids, rapid-setting polyurea polymer liquid system with a Shore A Hardness of A80-81. Edge-Pro 80 was developed to fill and protect joints in exposed concrete retail floors and in moderate-duty warehouse concrete floors. Its primary function is to protect joint edges from spalling under material handling vehicle traffic. Edge-Pro 80 is intended for use where final operating temperatures are from -20°F to +120°F. Edge-Pro 80 is also ideal for filling random cracks in exposed concrete retail floors and in moderate-duty warehouse concrete floors.

Information Links:

SRG Surface Refinement Grout Polished Concrete Floor Restoration Polymer

SRG is a two-component, 95% solids structural polyurethane/polyurea hybrid. When cured, SRG is a rigid structural polymer. Shore A Hardness: D70-75. SRG was developed to fill/repair concrete floor surface imperfections such as air holes, popouts, surface pitting, scratches, and gouges, etc. SRG is designed for use in commercial or retail polished concrete floors where final building temperatures are 32°F to +120°F.

Information Links:

Spal-Pro RS 65 Concrete Joint Sealant Ideal for Pedestrian and Cart Traffic

Spal-Pro RS 65 is a 100% solids, two-component rapid setting semi-rigid polyurea joint “sealant” intended for use in filling and protecting contraction and construction joints in retail or commercial concrete floors. Spal-Pro RS 65 was developed to seal floor joints in commercial/retail exposed concrete floors that are subject to pedestrian/cart traffic and very limited material handling traffic.

Information Links:

Rapid Refloor Low Viscosity Structural Polyurea/Polyurethane Hybrid Polished Concrete Repair

Repair Concrete Defects like Bolt Holes and Pop-Outs. Rapid Refloor is a 100% solids, two-component, low viscosity structural polyurea/polyurethane hybrid intended for use in repairing cracks and small surface defects such as bolt holes and pop-outs in industrial, retail or commercial concrete floors. Rapid Refloor’s rapid set chemistry allows for the return to service in 30 minutes or less. Compressive Strength: 4,000 psi. Rapid Refloor was developed to repair random cracks and surface spalls/pop-outs and other surface defects in industrial concrete floors that are subject to wheeled traffic. Rapid Refloor is designed for use in industrial or retail concrete floors where final building temperatures are 32 °F to 120 °F.

Information Links:

Rapid Refloor XP Fast Setting Extended Pot Life Concrete Repair

Extended Pot Life, Rapid Setting Structural Concrete Repair Product. Rapid Refloor XP is a two-component, 100% solids structural polyurethane/polyurea hybrid. When cured, Rapid Refloor XP is a rigid structural polymer with a Shore D Hardness of 75-80. Rapid Refloor XP was developed to repair a wide range of surface defects in industrial or stained/polished concrete floors including surface spalls/pop-outs, surface pitting, bolt-holes, random cracks, and more. Rapid Refloor XP is designed for use in industrial or stained/polished concrete floors where final building temperatures are 32°F to +120°F.

Information Links:

Rapid Refloor Pit Grout Concrete Floor Surface Repair Polymer

Repair Concrete Floor Imperfections. Rapid Refloor Pit Grout is a two-component, 100% solids structural polyurethane/polyurea hybrid.  When cured, Rapid Refloor Pit Grout is a rigid structural polymer with a Shore D Hardness of 70-75. Compressive Strength: 3550 psi. Rapid Refloor Pit Grout was developed to fill/ repair concrete floor surface imperfections such as air holes, pop-outs, surface pitting, scratches, and gouges, etc.  It can also be blended with dry aggregate to produce a repair mortar for various concrete deficiencies.  Rapid Refloor Pit Grout is designed for use in commercial or retail polished concrete floors where final building temperatures are 32°F to +120°F.

Information Links:

SPF and SPF-P Concrete Stain Protection for Polished and Stained Concrete Floors

SPF is a water-based single component film-forming liquid intended for use in the protection of concrete slab surfaces against staining which can result from epoxy joint filler overfill. SPF is water-soluble and can be easily removed after joint filler installation is completed. SPF-P will prevent staining in most polyurea fillers.

Information Links:

Products for Stained and Polished Concrete Floors

Need custom colored joint filler or surface repair materials for your colored concrete floor project? You can rely on Metzger/McGuire’s Industry Standard Floor Joint Fillers and Concrete Repair Products to provide your customer with surface restoration products manufactured to exacting color match standards and formulated to last for the life of the floor.

Since 1970 Metzger/McGuire has been an industry leader in providing industrial floor joint fillers and concrete floor repair materials to the industrial market and has built a reputation for providing the most durable and highest quality floor protection solutions the industry has to offer. We carry the same commitment and high-quality standards into providing floor joint fillers and concrete repair products into the decorative concrete floor industry. Whether you are working on a project for the largest retailer or for the homeowner, you can rely on Metzger/McGuire to provide floor restoration solutions for all of your decorative concrete flooring needs. Turning Point Supply has Metzger/McGuire product for polished concrete floor repair and polished concrete joint fillers in North Carolina and South Carolina at warehouses located in Charlotte and Raleigh.

Metzger McGuire Spal Pro RS 88 Polyurea Polished Concrete Joint Filler in North Carolina and South Carolina

Spal-Pro RS 88 is a rapid-setting polyurea polymer liquid of 100% solids content. When cured, Spal-Pro RS 88 is a gray, rubberlike solid with a hardness of Shore A86-90.

Basic Use

Spal-Pro RS 88 was developed to fill and protect joints in trafficked industrial and retail polished concrete floors. Its primary function is to support such traffic and protect joint edges. Spal-Pro RS 88 is intended for use where final temperatures are from freezing to over 120 degrees.

Spal-Pro RS 88 is Rated “Heavy-Duty” for polished concrete floor joint repair

Unlike softer polyureas, Spal-Pro RS 88’s higher shore hardness provides greater edge protection and support.

  • Spal-Pro RS 88 is “Rapid-Setting”

At 70˚F (21˚C) it can be opened to full traffic in as little as (60) minutes and light traffic in (30) minutes.

  • Spal-Pro RS 88 is Colorfast

Spal-Pro RS 88 maintains a consistent color profile and resists fading and other discoloration under normal conditions.

  • Spal-Pro RS 88 is Ideal for Use in Stained/Polished Floors

Spal-Pro RS 88 can be used to fill joints and cracks in polished concrete floors, and will not smudge or smear during grinding/polishing.

HARDNESS, SHORE “A” @ 70˚F D-2240 A86-90

TENSILE STRENGTH D-638 970 PSI

TENSILE ELONGATION*(@ 70˚F) D-638 180%

ADHESION TO CONCRETE D-4541 350-400 PSI

TACK FREE @ 70˚F – 5 Minutes

TRAFFIC READY @ 70˚ F – 1 Hour

MIX RATIO (by vol.) – 1:1

SOLIDS CONTENT – 100%

SHRINKAGE – Negligible

Metzger McGuire Edge Pro 80 Polished Concrete Joint Filler in North Carolina and South Carolina

Edge-Pro 80 is a two-part, 100% solids, rapid-setting polyurea polymer liquid system. When cured, Edge-Pro 80 is a rubberlike solid with a hardness of Shore A 80-81.

Basic Use

Edge-Pro 80 was developed to fill and protect joints in exposed concrete retail floors and in moderate-duty warehouse concrete floors. Its primary function is to protect joint edges from spalling under material handling vehicle traffic. Edge-Pro 80 is intended for use where final operating temperatures are from -20°F to +120°F.

Other Uses

Edge-Pro 80 is also ideal for filling random cracks in exposed concrete retail floors and in moderate-duty warehouse concrete floors.

Edge-Pro 80’s revolutionary new chemistry provides for superior substrate adhesion, moisture tolerance and a flusher finished profile compared to similar polyurea joint fillers.

Edge-Pro 80 Finishes Flusher with the Floor Surface

Edge-Pro 80’s chemistry permits for a wide shave window (15 min. to 24 hrs.) in which the installer can razor off overfill and achieve a consistently flush profile with floor surface.

Edge-Pro 80 is Moisture Tolerant

Edge-Pro 80 will not react with moisture and its special adhesionenhancers permit adhesion to damp substrates with minimal compromise as compared to dry substrates.

Edge-Pro 80 is Colorfast

Edge-Pro 80 maintains a consistent color profile and resists fading or discoloration under normal conditions.

Edge-Pro 80 is Ideal for Use in Stained/Polished Concrete Floors

Edge-Pro 80 can be ground and polished as early as 30 minutes (wet) and 3 to 4 hours (dry).

HARDNESS, SHORE A @ 70°F D-2240 80-81

TENSILE STRENGTH D-638 505 psi

TENSILE ELONGATION D-638 152%

VISCOSITY PART A POLYOL – 1535 cP

VISCOSITY PART B ISO – 2500 cP

TACK FREE @ 70°F – 3 minutes

GEL TIME @70°F – 35 seconds

TRAFFIC READY @70°F – 1 hour

MIX RATIO (BY VOL.) – 1:1

Metzger McGuire SRG Surface Refinement Grout for Polished Concrete Floor Repair in North Carolina and South Carolina

SRG is a two-component, 95% solids structural polyurethane/ polyurea hybrid. When cured, SRG is a rigid structural polymer with a Shore D Hardness of 70-75.

Basic Use:

SRG was developed to fill/repair micro-level concrete floor surface imperfections such as air holes, sand aggregate pops, surface pitting, scratches and gouges, etc. SRG can also be mixed with sand aggregate

to create a repair mortar suitable for joints, cracks, and larger surface defects. SRG is designed for use in commercial or retail polished concrete floors where final building temperatures are 32°F (0°C) to +120°F (49°C). SRG is designed for use with a Color Pack. An Accelerator Pack which reduces potlife and grind time is also available.

Available in 9 colors to best camouflage floor surface pitting and surface imperfections. Rapid-set formula allows for quick access to floor areas and grinding as early as 40 minutes after application (@70°) or 20 minutes with Accelerator Pack. Low viscosity allows for penetration into very small

surface pits and imperfections Yields a smoother, denser floor surface which can aid in achieving higher gloss and DOI values.

Viscosity Profile

Part A 199 cps

Part B 178 cps

Mixed 190 cps

Reaction Profile

Pot life 5 minutes

(100 grams at 74°F)

Working time (on floor) 5-8 minutes

Tack-Free Time 20-30 minutes

Grindable 40 minutes

Typical Physical Properties

Shore D Hardness 70-75

Compressive Strength (ASTM D-638), psi. 4767

Tear Strength (ASTM D-624), psi 284

Tensile Strength (ASTM D-412), psi 4184

Elongation (ASTM D-412), % 2.8

VOC Content 47 g/l

Mix Ratio by Volume 1:1

Odor Minimal

Shrinkage Negligible

Metzger McGuire Spal Pro RS 65 Polished Concrete Floor Joint Filler Repair Material in North Carolina and South Carolina

Spal-Pro RS 65 is “Rapid-Setting”

At 70°F (21°C) Spal-Pro RS 65 can be opened to pedestrian traffic in as little as (30) minutes and full traffic in (60) minutes.

Spal-Pro RS 65 Provides Anti-Microbial Protection

Spal-Pro RS 65’s anti-microbial additives inhibit the growth of microbes such as viruses, bacteria or fungi.

Spal-Pro RS 65 is Colorfast

Spal-Pro RS 65 maintains a consistent color profile and resists fading and other discoloration under normal conditions.

Spal-Pro RS 65 Can Be Used with Grinding/Polishing Systems

Unlike most sealants, Spal-Pro RS 65 should not smear under most concrete grinding/polishing conditions, and its rapid set properties allow for grinding/polishing operations to commence as early as 60 minutes after filler placement (at 70°F).

Spal-Pro RS 65 Reduces Incidence of Filler Separation

Spal-Pro RS 65’s lower Shore A hardness provides greater lateral movement capability to reduce the occurrence of filler separation voids normally associated with semi-rigid joint fillers when concrete shrinkage/joint opening occurs.

HARDNESS, SHORE “A” @ 70°F D-2240 A64-69

INITIAL GEL TIME – 50 SEC.

FULL GEL TIME – 2 MINS.

PEDESTRIAN TRAFFIC – 30 MINS.

INITIAL SHAVE TIME – 1 HOUR

INITIAL GRINDING/POLISHING – 6 HOURS

TENSILE ELONGATION*(@ 70°F) D-412 162%

TENSILE STRENGTH (@ 70°F) D-412 393 psi

MIX RATIO (by vol.) – 1:1

SOLIDS CONTENT – 100%

SHRINKAGE – Negligible

Metzger McGuire Rapid Refloor Polished Concrete Control Joint Color Repair Material for North Carolina and South Carolina

Rapid Refloor is a two-component, 100% solids, structural polyurethane/polyurea hybrid. When cured,

Rapid Refloor is a rigid structural polymer with a Shore D Hardness of 70-75.

Basic Use: Rapid Refloor was developed to repair random cracks and surface spalls/popouts and other surface defects in industrial concrete floors that are subject to wheeled traffic. Rapid Refloor is designed for use in industrial or retail concrete floors where final building temperatures are 32°F to +120°F.

Permanent, durable structural concrete repair in minutes. Ready for traffic in 15 – 30 minutes. Can be ground flush with floor in 25 minutes. Rapid Refloor’s low-viscosity allows for penetration into cracks as narrow as 1/64” (.016”). Unlike many low-viscosity structural repair products, Rapid Refloor is virtually odorless. Rapid Refloor is non-hazardous and can be shipped overnight by air carrier.

Viscosity Profile

Part A 120 cps

Part B 70 cps

Mixed 100 cps

Reaction Profile

(100 grams, 74°F/23°C Sample)

Gel Time, minutes 1-1.25

Tack-Free Time, minutes 5-8

Traffic Ready, minutes 15-30

Typical Physical Properties

Shore D Hardness 70-75

Compressive Strength (ASTM D-638), psi 4000

Tensile Strength (ASTM D412), psi 5500

Elongation (ASTM D412), % 6.0-8.0

Die C Tear Strength (ASTM D624), pli 400

Mix Ratio by Volume 1:1

Odor Odorless

Shrinkage Negligible

Metzger McGuire Rapid Refloor XP Extended Pot Life Polyurea Joint Repair Material for Polished Concrete Floors in North Carolina and South Carolina

Rapid Refloor XP is a two-component, 100% solids, structural polyurethane/polyurea hybrid. When cured, Rapid Refloor XP is a rigid structural polymer with a Shore D Hardness of 75-80.

Basic Use:

Rapid Refloor XP was developed to repair a wide range of surface defects in industrial or stained/polished concrete floors including surface spalls/popouts, surface pitting, bolt-holes, random cracks and more. Rapid Refloor XP is designed for use in industrial or stained/polished concrete floors where final building temperatures are 32°F (0°C) to +120°F (49°C).

Permanent, durable, structural concrete repair in minutes.

  • Ready for traffic in 60-120 minutes depending on application Rapid Refloor XP’s low viscosity allows for penetration into cracks as narrow as 1/64” (.016 or .40 mm) and micropits in the floor surface.
  • Unlike many low-viscosity structural repair products, Rapid Refloor XP is virtually odorless.
  • Rapid Refloor XP is non-hazardous and can be shipped overnight by air carrier.
  • When used as a grouting product, Rapid Refloor XP can enhance floor surface continuity and gloss.
  • Rapid Refloor XP can be mixed with aggregate to extend yield and provide better blended repairs.

Viscosity Profile

Part A 640 cps

Part B 40 cps

Mixed 340 cps

Reaction Profile

(100 grams, 74°F/23°C Sample)

Pot life 3 1/2-4 minutes

Tack Free Time 5-8 minutes

Traffic Ready 60-120 minutes

Typical Physical Properties

Shore D Hardness 75-80

Compressive Strength (ASTM D-695), psi 4190

Tensile Strength (ASTM D638), psi 4300

Elongation at break (ASTM D638), % 14-18

Mix Ratio by Volume 1:1

Odor Odorless

Shrinkage Negligible

Metzger McGuire Rapid Refloor Pit Grout Polished Concrete Surface Repair Material for North Carolina and South Carolina

Rapid Refloor Pit Grout is a two-component, 100% solids, structural polyurethane/polyurea hybrid.  When cured, Rapid Refloor Pit Grout is a rigid, structural polymer with a Shore D Hardness of 70-75.

Basic Use:

Rapid Refloor Pit Grout was developed to fill/repair concrete floor surface imperfections such as air holes, popouts, surface pitting, scratches and gouges, etc. It can also be blended with dry aggregate to produce a repair mortar for various concrete deficiencies. Rapid Refloor Pit Grout is designed for use in commercial or retail polished concrete floors where final building temperatures are 32°F to +120°F.

Available in over 48 ColorFast colors to best camouflage floor surface pitting and surface imperfections. Rapid-set formula allows for quick access to floor areas and grinding as early as 45 minutes after application. Low-viscosity allows for penetration into very small, micro-level surface pits and imperfections. Yields a smoother, denser floor surface 100% solids, minimal odor formula.

Viscosity Profile

Part A 228 cps

Part B 50 cps

Mixed 139 cps

Reaction Profile

Pot life in Mixing Nozzle (70°F/21°C) 1-1.5 minutes

(Thin Film, 70°F/21°C Sample)

Working time 3-4 minutes

Tack Free Time 15 minutes

Grindable 45 minutes

Typical Physical Properties

Shore D Hardness 70-75

Compressive Strength (ASTM D-638), psi 3550

Tensile Strength (ASTM D412), psi 5100

Elongation (ASTM D412), % 7.0-9.0

Die C Tear Strength (ASTM D624), pli 380

Mix Ratio by Volume 1:1

Odor Minimal

Shrinkage Negligible